Teknor Apex TELCAR® 1000-92UV Thermoplastic Elastomer物性表-搜物性

物理性能	额定值 (公制)	额定值 (英制)	测试方法
比重	g/cc	g/cc	+/- 0.02; ASTM D792
线性成型收缩率	cm/cm	in/in	24 hours; ASTM D955
	cm/cm	in/in	After 30 min. at 180°F; ASTM D955
熔体流动速率	g/10 min @Load 2.16 kg, Temperature 230 °C	g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238

机械性能	额定值 (公制)	额定值 (英制)	测试方法
肖氏硬度 (邵氏 D)			10 second delay. +/- 3; ASTM D2240
抗张强度(断裂)	MPa	psi	20"/min Type 1; ASTM D412
抗张强度(屈服)	MPa	psi	ASTM D412
	MPa	psi	107% Retention, Air Oven Aged 42 days at 121°C
	MPa	psi	110% Retention, Air Oven Aged 42 days at 110°C
伸长率 (断裂)
			33% Retention, Air Oven Aged 42 days at 110°C
			37% Retention, Air Oven Aged 42 days at 121°C
			ASTM D412
屈服伸长率			ASTM D412
100% 模量	GPa	ksi	ASTM D412
300％模量	GPa	ksi	ASTM D412
弯曲模量	GPa	ksi	ASTM D790
悬壁梁缺口冲击强度			Heat Aging Performance 1000 hrs at 120°C
	@Temperature -40.0 °C	@Temperature -40.0 °F	Heat Aging Performance 1000 hrs at 120°C
加德纳冲击	J @Temperature -30.0 °C	ft-lb @Temperature -22.0 °F
拉伸冲击强度	>= kJ/m²	>= ft-lb/in²
冲击试验	J @Temperature -40.0 °C	ft-lb @Temperature -40.0 °F	At Yield. Deflection: 693 mils, Force: 425 lbs (Instrumented Impact, 9000 in/min)
	J @Temperature -40.0 °C	ft-lb @Temperature -40.0 °F	At Break. Deflection: 1359 mils, Failure Mode: Ductile (Instrumented Impact 9000 in/min)
撕裂强度	kN/m	pli	Die C; ASTM D1004

热性能	额定值 (公制)	额定值 (英制)	测试方法
线性热膨胀系数	µm/m-°C @Temperature -30.0 - 30.0 °C	µin/in-°F @Temperature -22.0 - 86.0 °F
线性热膨胀系数,横向流动	µm/m-°C @Temperature -30.0 - 30.0 °C	µin/in-°F @Temperature -22.0 - 86.0 °F
载荷下热变形温度(0.46 MPa)	°C	°F
载荷下热变形温度(1.8 MPa)	°C	°F
玻璃化转变温度，Tg	°C	°F
Flame Spread	mm/min	in/min	Pass: Burn Rate- Max 100; FMVSS 302

材料描述		测试方法
Fogging	92, 3 hours at 100°C, Haake buchler

Teknor Apex TELCAR® 1000-92UV Thermoplastic Elastomer