Azoty Tarnow™ Tarnamid® T-27 CF10 Polyamide 6 10% Carbon Fiber - Antistatic and Electroconductive

Medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.

Electroconductive grade based on carbon fiber reinforcement, very high stiffness and strength.

Tarnamid® has the following main properties:

• High mechanical strength, rigidity and hardness
• High impact strength
• High vibration damping capacity
• Good fatigue strength
• Very good sliding properties, abrasion resistance, low coefficient of friction
• High thermal resistance, admissible temperature of continuous operation from -60°C to +150°C
• High chemical resistance, particularly to organic solvents, oils, lubricants and fuels
• Considerable moisture absorption influencing mechanical and electrical properties
• Self-extinguishing properties (fire retardant properties)
• Good electro-insulating properties
• Good optical properties, relatively good transparency of molded pieces with thickness below 3.2 mm made from natural Tarnamid® (not dyed and not compounded)
• Can be used for the production of goods coming into contact with food (grades fulfilling requirement of European Union Directive No 2002/72/EEC) with latest amendments

Information provided by Azoty Tarnow™.

物理性能	额定值 (公制)	额定值 (英制)	测试方法
比重	g/cc	g/cc	ISO 1183
线性成型收缩率,Flow	cm/cm	in/in	ISO 294-4
线性成型收缩率，横向	cm/cm	in/in	ISO 294-4
熔体流动速率	g/10 min @Load 5.00 kg, Temperature 275 °C	g/10 min @Load 11.0 lb, Temperature 527 °F	ISO 1133

机械性能	额定值 (公制)	额定值 (英制)	测试方法
球压硬度	MPa @Load 36.5 kg	psi @Load 80.5 lb	ISO 2039-1
抗张强度	MPa	psi	ISO 527
伸长率 (断裂)			ISO 527
拉伸模量	GPa	ksi	ISO 527
弯曲强度	<= MPa	<= psi	ISO 178
简支梁无缺口冲击强度	J/cm²	ft-lb/in²	ISO 179 1eU
简支梁缺口冲击强度	J/cm²	ft-lb/in²	ISO 179 1eA

电气性能	额定值 (公制)	额定值 (英制)	测试方法
表面电阻	ohm	ohm	IEC 93

热性能	额定值 (公制)	额定值 (英制)	测试方法
熔融温度	°C	°F
载荷下热变形温度(1.8 MPa)	°C	°F	ISO 75
维卡软化温度	°C @Load 5.10 kg	°F @Load 11.2 lb	ISO 306
可燃性(UL94)	@Thickness 1.60 mm	@Thickness 0.0630 in

加工性能	额定值 (公制)	额定值 (英制)	测试方法
加工（熔体）温度	°C	°F
模具温度	°C	°F	80 - 90°C is recommended
干燥温度	°C @Time 7200 - 14400 sec	°F @Time 2.00 - 4.00 hour
水分含量
注射压力	MPa	psi	80 MPa is recommended