Recommended Primer: Dow Corning S2260
This data represents typical values for the production material and should not be used as material specifications.Information provided by ARLON Silicone Technologies Division.
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | g/cc | lb/in³ | Silicone Property; Arlon SQA-TMS-024 |
| 厚度 | microns | mil | Carrier |
| microns | mil | Product; Arlon SQA-TMS-003 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 A) | Silicone Property; ASTM D2240 | ||
| 抗张强度 | MPa | psi | Silicone Property; ASTM D412 |
| 伸长率 (断裂) | Silicone Property; ASTM D412 | ||
| 弹性模量 | GPa | ksi | Arlon SQA-TMS-008 |
| 泊松比 | |||
| 剪切模量 | <= GPa | <= ksi | Arlon SQA-TMS-018 |
| 剪切强度 | MPa | psi | Lap; ASTM D1002 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 介电常数 | @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | IPC TM 650 - 2.5.5.3 |
| 介电强度 | kV/mm | kV/in | ASTM D149 |
| 耗散因数 | @Frequency 1.00e+6 Hz | @Frequency 1.00e+6 Hz | IPC TM 650 - 2.5.5.3 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线性热膨胀系数 | µm/m-°C | µin/in-°F | ASTM E831 |
| 比热容 | J/g-°C | BTU/lb-°F | E1461-01 |
| 导热系数 | W/m-K | BTU-in/hr-ft²-°F | ASTM E1530 |
| Maximum Service Temperature, Inert | °C | °F | |
| 最低工作温度, Air | °C | °F | |
| 玻璃化转变温度，Tg | °C | °F | ASTM E1356 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 固化时间 | min @Temperature 121 °C | hour @Temperature 250 °F | Recommended Cure Cycle; Under Pressure |
| 保质期 | Month @Temperature 7.22 °C | Month @Temperature 45.0 °F |
| 材料描述 | 测试方法 | |
|---|---|---|
| 颜色 | White | |
| Thermal Resistance (°C-in2/W) | 0.5 | ASTM E1530 |
| 产品总重量（oz/yd2） | 19 | Arlon SQA-TMS-025 |