Chevron Phillips Marlex® C513UV High Density Polyethylene, Blow Molding物性表-搜物性

This extra high molecular weight, hexane copolymer is tailored for intermediate bulk container applications that require:

Typical applications for C513UV include blow molded items such as:

This resin meets these specifications:

ASTM D4976 - PE 235
FDA 21 CFR 177.1520(c) 3.1a, use conditions C through G per 21 CFR 176.170(c). Volume of food containing article must be equal to or greater than 5 gallons.

Information provided by Chevron Phillips Chemical Company LP.

搜物性提供30万余种物性表数据，如要查看关于 Chevron Phillips Marlex® C513UV High Density Polyethylene, Blow Molding 完整物性数据，以及其替代物，黄卡信息，下载物性表PDF.

请获得完整功能体验。

物理性能	额定值 (公制)	额定值 (英制)	测试方法
比重	g/cc	g/cc	ASTM D1505
ESCR 100% Igepal®	>= hour	>= hour	Condition A, F50; ASTM D1693
	>= hour	>= hour	Condition B, F50; ASTM D1693
熔体流动速率	g/10 min @Load 21.6 kg, Temperature 190 °C	g/10 min @Load 47.6 lb, Temperature 374 °F	ASTM D1238

机械性能	额定值 (公制)	额定值 (英制)	测试方法
肖氏硬度 (邵氏 D)			ASTM D2240
抗张强度(屈服)	MPa	psi	2 in/min, Type IV bar; ASTM D638
伸长率 (断裂)			2 in/min, Type IV bar; ASTM D638
弯曲模量	GPa	ksi	Tangent; ASTM D790
拉伸冲击强度	kJ/m²	ft-lb/in²	ASTM D1822

热性能	额定值 (公制)	额定值 (英制)	测试方法
载荷下热变形温度(0.46 MPa)	°C	°F	ASTM D648
维卡软化温度	°C	°F	ASTM D1525
脆化温度	<= °C	<= °F	Type A clamp, Type I Specimen; ASTM D746

此数据表中的信息由搜聚从该材料的生产商处获得。搜聚尽最大努力确保此数据的准确性。但是搜聚对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。

Chevron Phillips Marlex® C513UV High Density Polyethylene, Blow Molding