Adiprene® L 767

ADIPRENE L 767 is a TDI polyether-based liquid urethane prepolymer which is readily processable by conventional hand and machine mixing techniques. ADIPRENE L767 produces high quality elastomers in the 62D durometer hardness range when cured with 4,4'-methylene-bis (2-chloroaniline), and the 53 D durometer hardness range when cured with CAYTUR® 21DA.

These tough, highly resilient elastomers have many unique features:

• Excellent low-temperature flexibility

?- Excellent abrasion resistance
?- Good hydrolytic stability
?- Good compression set resistance

These properties suggest the use of ADIPRENE L 767 in applications such as wheels, rolls, or spraying.

基本信息
特性	低温下的柔性 良好耐磨损性 韧性良好 水解稳定 有弹性
用途	车轮
形式	液体
加工方法	浇铸 可喷涂 压缩模塑 真空铸造

物理性能	额定值	单位制	测试方法
比重		g/cm³	ASTM D792

硬度	额定值	单位制	测试方法
肖氏硬度 (邵氏 D)			ASTM D2240

弹性体	额定值	单位制	测试方法
拉伸应力 (100%应变)		MPa	ASTM D412
抗张强度		MPa	ASTM D412
伸长率 (断裂)		%	ASTM D412
撕裂强度 (开裂)		kN/m	ASTM D470
压缩永久变形 (70°C, 22 hr)		%	ASTM D395B
巴肖氏弹性		%	ASTM D2632
卡-伯模量			ASTM D1043
-57°C		MPa	ASTM D1043
-40°C		MPa	ASTM D1043
-18°C		MPa	ASTM D1043
24°C		MPa	ASTM D1043

热固性	额定值	单位制
热固组件
树脂
硬化法
储存稳定性		min
后固化时间 (70°C)		hr

补充信息	额定值	单位制
Abrasion Index - NBS

Uncured Properties	额定值	单位制
固化时间 (100°C)		hr